Cemedine SX-PPK1000(EXP) 333ml

Cemedine SX-PPK1000(EXP) 333 ML/Cartridge

Features

1. Designed for polypropylene (PP) materials
   Excellent adhesion to polypropylene resin, which is normally adhesive-resistant.
    
2. One-part type
   Does not require primer application ,improving the work environment and increasing work efficiency.
    
3. Adhesive for bonding different types of materials
   Excellent adhesion to polypropylene resin and various other materials. This is an elastic adhesive which can ease thermal stress caused by a difference in thermal expansion coefficient among different types of materials.
    
4. Flexible Cured properties
   Designed for cured film properties that are excellent in flexibility and followings, and has excellent peel adhesion.

   Application

5. For bonding polypropylene resin with different types of materials.
   (Not suited for bonding materials such as polyethylene, fluorine, and polyacetal)
6. For bonding that requires durability (e.g. in relation to thermal cycles).
7. For bonding that requires waterproof performance.
8. For bonding related to PP automotive parts, and electrical components and parts.

9. Comparison with conventional adhesives

   	Surface treatment method		SX-PPK1000(EXP)	Conventional adhesive
   Tensile shear strength (MPa) PP×PP	Untreated		1.4	0.3
   	Treated with PP dedicated primer		Unnecessary	2.8
   	Treated with Corona discharge	(Once)	Unnecessary	0.7
   		(2 Times)		1.3
   180°degree peel strength (N/25mm ) PP×Canvas	Untreated		75	3
   	Treated with PP dedicated primer		Unnecessary	50
   	Treated with Corona discharge	(Once)	Unnecessary	10
   		(2 Times)		30

   Tensile shear strength
   Curing : 23°C50%RH x 7 days
   Coating quantity : Coated on both sides 100μm thick (per side)
   Application area : 25mm x 25mm
   Tension speed: 50mm/min

   180°degree peel strength
   Curing : 23°C50%RH x 7 days
   Coating quantity: Coated on both sides 300μm thick (per side)
   Pressing : Rubber roller
   Tension speed : 200mm/min

   Product data

   Tensile shear adhesive strength of PP (homopolymer) and various adherends

   (MPa)

   PP (Homopolymer ) ×The following adherends	Tensile shear strength
   PP	1.4	CF5 AF5
   PP (TALC 10wt%)	1.6	CF
   PVC	1.3	CF9 AF1(PP)
   PC	1.4	CF9 AF1(PP)
   ABS	1.4	CF6 AF4(PP)
   PMMA	1.6	CF8 AF2(PP)
   PA6	1.3	CF8 AF2(PP)
   SPCC	1.5	CF1 AF9(SPCC)
   AL	1.6	CF
   PET	1.6	CF
   PBT	1.6	CF
   PPO	1.5	CF8 AF2(PP)
   PPS	1.1	CF3 AF7(PPS)
   POM	1.1	CF3 AF7(POM)
   PA MXD6	1.3	CF5 AF5(MXD6)
   PEEK	2.2	CF
   FRP	1.6	CF
   SUS304 2B	0.8	AF(SUS)

   CF:Cohesion Failure, AF:Adhesive Failure

   The numbers indicate their proportion to the adhesion area.
   Parentheses in the case of AF indicate adherends in which Adhesive Failure has occurred.

   Curing : 23°C50%RH x 7 days
   Coating quantity : Coated on both sides 100μm thick (per side)
   Application area : 25mm x 25mm
   Tension speed : 50mm/min
   Destruction State : Confirmation by seeing

   Tensile shear adhesive strength of PP talc (PP containing 10% talc) and various adherends

   (MPa)

   PP (TALC)  x The following adherends	Initial state		80°C x 1week		80°C85%RH x 1week
   PP (TALC)	1.6	CF	2.1	CF8 AF2(PP)	1.9	CF
   ABS	1.6	CF	2.1	CF4 AF6(ABS)	1.9	CF
   PMMA	1.5	CF	2.2	CF9 AF1(PP)	1.8	CF
   PBT	1.7	CF8 AF2(PP)	2.2	CF	1.8	CF
   PPO	1.7	CF9 AF1(PP)	2.2	CF	2.0	CF
   PPS	1.1	CF2 AF8(PPS)	2.2	CF	2.0	CF
   POM	1.0	CF3 AF7(POM)	1.0	CF2 AF8(POM)	1.0	CF2 AF8(POM)
   PA MXD6	1.6	CF	2.2	CF3 AF7(RENY)	1.4	CF2 AF8(RENY)
   SUS304 2B	0.7	AF(SUS)	2.2	CF3 AF7(SUS)	1.7	CF3 AF7(SUS)
   Aluminum	1.7	CF8 AF2(PP)	2.2	CF	2.0	CF
   Copper	1.6	CF2 AF8(Cu)	2.0	CF	1.9	CF

   CF:Cohesion Failure, AF:Adhesive Failure

   The numbers indicate their proportion to the adhesion area.
   Parentheses in the case of AF indicate adherends in which Adhesive Failure has occurred.

   Curing : 23°C50%RH x 7 days
   Open time : 5 min (10 min for metal / PP)
   Coating quantity : Coated on both sides 100μm thick (per side)
   Tension speed : 50mm/min
   Destruction State : Confirmation by seeing
   Pressing : 2 pinches

   Peeling adhesion strength with various adherends

   (N/25mm)

   Adherends x Canvas 180°degree peel strength	Initial state (23°C50%RH x 1week)		Initial state + 80°C x 1week		Initial state  + 80°C85%RH x 1week
   PP	75.3	CF7 AF3	84.2	CF	132.0	CF9 AF1
   PP (TALC 10wt%)	93.1	CF3 AF7	129.8	CF5 AF5	129.2	CF
   PC (Glass fiber 30wt%)	88.3	CF	108.4	CF	132.4	CF
   ABS	85.3	CF	105.4	CF	118.0	CF
   PC/ABS	92.0	CF	111.5	CF	127.5	CF
   PMMA	90.9	CF	111.6	CF	124.1	CF
   PA MXD6	107.3	CF	113.3	CF	52.8	AF
   PBT	80.2	CF	116.0	CF	118.5	CF
   PPO	87.5	CF	118.4	CF	130.5	CF
   PPS	89.7	CF	108.7	CF	131.0	CF
   PEEK	94.1	CF	102.5	CF	110.8	CF
   POM	67.9	CF5 AF5	83.5	CF5 AF5	46.5	CF1 AF9
   SPCC-SD	73.8	CF1 AF9	111.0	CF	110.8	CF
   SUS304 2B	41.6	AF	120.7	CF6 AF4	129.1	CF

   Tension speed : 200mm/min
   Destruction State : Confirmation by seeing

   Thermal shock test

   Tensile shear adhesive strength (MPa)

   	PP x ABS		PP x AL
   Initial state	1.4	CF6 AF4(PP)	1.6	CF
   100 cycles	1.9	CF7 AF4(PP)	2.0	CF7 AF3(PP)
   250 cycles	1.9	CF1 AF9(PP)	2.2	CF6 AF4(PP)
   500 cycles	2.3	CF2 AF8(PP)	2.8	CF6 AF4(PP)
   750 cycles	2.2	CF2 AF8(PP)	2.2	CF5 AF5(PP)
   1000 cycles	1.8	CF1 AF9(PP)	2.7	CF4 AF6(PP)
   1500 cycles	1.8	CF2 AF8(PP)	2.5	CF4 AF6(PP)

   CF:Cohesion Failure, AF:Adhesive Failure

   The numbers indicate their proportion to the adhesion area.
   Parentheses in the case of AF indicate adherends in which Adhesive Failure has occurred.

   Curing : 23°C50%RH x 7 days
   Coating quantity : Coated on both sides 100μm thick (per side)
   Application area : 25mm x 25mm
   Tension speed : 50mm/min
   Destruction State : Confirmation by seeing

   Heat or cold aging test

   Tensile shear adhesive strength (MPa)

   	-35°C (PP x AB)		-35°C (PP x AL)		100°C (AL x AL)		120°C (AL x AL)
   Initial	1.4	CF6 AF4(PP)	1.6	CF	1.9	CF	1.9	CF
   1 week	2.2	CF8 AF2(PP)	2.2	CF7 AF3(PP)	3.7	CF	3.3	CF
   2 weeks	2.2	CF7 AF3(PP)	2.2	CF7 AF3(PP)	3.5	CF	3.9	CF
   4 weeks	2.3	CF7 AF3(PP)	2.1	CF6 AF4(PP)	3.4	CF	3.9	CF
   8 weeks	2.2	CF8 AF2(PP)	2.1	CF7 AF3(PP)	3.5	CF	3.9	CF

   CF:Cohesion Failure, AF:Adhesive Failure

   The numbers indicate their proportion to the adhesion area. Parentheses in the case of AF indicate adherends in which Adhesive Failure has occurred.

   Curing: 23°C50%RH x 7 days 
   Test conditions : After curing, leave under each temperature condition 
   Coating quantity : Coated on both sides 100μm thick (per side) 
   Application area : 25mm x 25mm 
   Tension speed : 50mm/min 
   Destruction State : Confirmation by seeing

   Property

   			SX-PPK1000(EXP)
   Application / Properties / Features			Designed for polypropylene (PP) materials
   Type			One-part moisture-curing elastic adhesive
   Base			Acrylic modified silicone
   Appearance			Slightly yellowish-white paste
   Viscosity		Pa･s/23°C	120
   Density		g/cm3	1.23
   Skin over time		23°C	15 min
   Depth curing		ｍｍ	1.63
   Tensile shear strength	PP(Talc 10wt%)	MPa	1.6
   180° degree peel strength	PP(Talc 10wt%) x Canvas	N/25mm	93.1
   Curing properties	Hardness	Shore A	15
   	Breaking strength	MPa	1.2
   	Elongation at break	%	875
   Capacity			333ml