Cemedine Super X is an innovative one-part, quick cure adhesive with three key features: "Pressure-sensitive adhesion", "Elastic adhesion" and "Solvent-free adhesion", which are the ideal properties of adhesives. It is used around the world.
Features
Multi-purpose adhesive for high-performance bonding of numerous materials.
Super X products allow for adhesion of various types of plastics, rubbers and ceramics over an extensive range, and also over different types of metals. These products provide excellent adhesion over a very extensive range of materials, eliminating the need for selecting a particular adhesive for each type of material, as in the case of conventional adhesives.
One-part solventless type providing quick curing at room temperature
Curing reaction is caused by moisture absorbed from the air. Pressure-sensitive range is reached in this curing process about 10 min after application. If adherends are put together during this time, they bind instantaneously as in the case of rubber contact adhesive, eliminating the need for temporary fixation. Easy-to-use, safe, and clean adhesive featuring one-part solventless capable of quick curing at room temperature is provided.
High durability
Super X as elastic adhesives does not peel off. Once materials are adhered, Super X provides durability in the range from low temperature (-60°C) to high temperature (120°C). Because of the rubber state of the hard film, the Super X sufficiently follows expansion, shrinkage and other changes of adherends.
Siloxane-free
There is not including low molecular weight cyclosiloxane. (D3 to D10 Cyclosiloxane compound)
Application
For bonding application that requires initial rise strength.
For bonding applications of dissimilar materials with different coefficients of thermal expansion.
For bonding applications that require durability, such as thermal cycling.
There are two ways to use: single sided and double sided. Please use properly depending on the material and the conditions to be attached.
Coated on both sides, 50µm thick (one side),tension speed between adherends: 50mm/min
*1 and *2: Surface preparation causes adhesive strength to become uneven; it must be confirmed in advance. *3: Primer (Cemedine PP-7F) to be used.
Adhesive strength for various types of rubbers
(N/mm)
Adherends
Peeling adhesive strength after 7-day curing
Rubbers
NBR
0.27
AF
Silicone rubber
0.45
AF
EPDM
0.60
AF
EPDM(*)
2.73
CF
CR (Chloroprene rubber) (*)
0.43
AF
(*)…Degreasing by MEK after treatment by sandpaper (#120)
Chemicals resistance
(MPa)
Chemicals
Tensile shear strength after dipping in chemicals
Initial Value
2.24
AF
Water
3.00
CF5 AF5
Acetic acid (1% water solution)
2.05
CF4 AF6
Acetic acid (10% water solution)
1.22
CF3 AF7
Sulfuric acid (3% water solution)
2.93
CF2 AF8
Sulfuric acid (30% water solution)
2.05
AF
Sodium hydroxide (1% water solution)
2.84
CF5 AF5
Sodium hydroxide (10% water solution)
3.29
CF2 AF8
Machine oil (Idemitsu: Mechanic Oil)
2.96
CF5 AF5
Salt (10% water solution)
3.16
CF4 AF6
MEK*
0.11
AF
n-Hexane*
0.56
AF
CF:Cohesion Failure, AF:Adhesive Failure
Adherends : Stainless steel x Stainless steel Surface preparation : Degreasing with MEK Coating quantity : Coated on both sides 50μm thick (per side) Open time : 2 min Pressing : 2 pinches Curing : 23°C50%RH x 7 days Chemical immersion : 23°C x 7 days Tension speed : 50 mm/min Destruction State : Confirmation by seeing *… Deterioration of solvent is observed, but no problem with short-time contact, for example, in washing.