Reactive Acrylic Adhesive
The two-part acrylic adhesive, whose curing properties do not change much even if the mixing ratio and mixing status vary, has user friendliness almost equal to that of one-part adhesive.
Features
- Reactive acrylic adhesive has the robust strength of a structural adhesive.
- Reactive acrylic adhesive is cured quickly.
- Reactive acrylic adhesive contains no inflammable solvent.
- Reactive acrylic adhesive does not have as bad an odor as a conventional acrylic adhesive.
- Reactive acrylic adhesive causes almost no skin irritation. unlike epoxy adhesive.
- The adhesive property of reactive acrylic adhesive is unchanged, even on a slightly oily surface.
Application
- Assembly of building members
- Assembly of signboard
- Assembly of furniture
- Adhesion and assembly of automotive and vehicle parts
- Assembly of magnets
- Assembly of sports goods
Product details
・Multi-purpose type : Y600, Y600H, Y610, Y620
・High heat resistance type : Y611BLACK S, Y612BLACK
・Flexible type : Y618LD, Y618H, Y630D
・Conventional type (*Odorous) : Y650
Product data
Adhesive strength by mixing ratio
Oil surface adhesion
Heat aging resistance
High temperature high humidity durability
Heat shock testing
Chemical resistance
Property
Multi-purpose type
| |
Y600 |
Y600H |
Y610 |
Y620 |
| Agent A |
Agent B |
Agent A |
Agent B |
Agent A |
Agent B |
Agent A |
Agent B |
| Application / Properties / Features |
High speed curing |
High viscosity |
High strength |
Slow curing |
| Base |
Acrylic resin |
Acrylic resin |
Acrylic resin |
Acrylic resin |
| External appearance |
Light blue |
Blue |
White |
Gray |
White |
Gray |
Light yellow |
Blue |
| Viscosity |
mPa･s/23°C |
4,000 |
4,000 |
30,000 |
30,000 |
5,500 |
5,500 |
8,000 |
8,000 |
| Mixing ratio |
1:1 |
1:1 |
1:1 |
1:1 |
| Pot life *1 |
23°C |
30 s |
2 min |
3 min |
6 min |
| Set time *2 |
23°C |
3 min |
4 min |
6 min |
20 min |
| Adhesive property |
Tensile shear strength |
MPa |
23.2 |
19.4 |
26.0 |
21.1 |
| T-peel strength |
N/mm |
5.0 |
3.6 |
3.7 |
4.2 |
| Curing properties |
Hardness |
Shore A |
68 |
65 |
72 |
66 |
| Glass transfer point |
°C |
83 |
78 |
90 |
79 |
| Elastic modulus |
MPa |
767 |
742 |
935 |
778 |
| Breaking strength |
MPa |
16.2 |
14.0 |
19.0 |
16.1 |
| Elongation at break |
% |
26 |
8 |
6 |
25 |
| Capacity |
600g set |
50g set |
50g set |
600g set |
| |
10kg |
600g set |
2kg |
| |
|
|
|
| |
|
|
|
|
*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).
High heat resistance type
| |
Y611BLACK S |
Y612BLACK |
| Agent A |
Agent B |
Agent A |
Agent B |
| Application / Properties / Features |
Hight strength / High heat resistance |
| Base |
Acrylic resin |
Acrylic resin |
| External appearance |
Light yellow |
Black |
Light yellow |
Black |
| Viscosity |
Pa･s/23°C |
3,000 |
3,000 |
15,000 |
15,000 |
| Mixing ratio |
1:1 |
1:1 |
| Pot life *1 |
23°C |
3 min |
1 min |
| Set time *2 |
23°C |
7 min |
3 min |
| Adhesive property |
Tensile shear strength |
MPa |
28.4 |
29.2 |
| T-peel strength |
N/mm |
4.2 |
4.3 |
| Curing properties |
Hardness |
Shore D |
84 |
86 |
| Glass transfer point |
°C |
123 |
127 |
| Elastic modulus |
MPa |
1558 |
1615 |
| Breaking strength |
MPa |
32.9 |
33.7 |
| Elongation at break |
% |
3.5 |
3.2 |
| Capacity |
600g set |
600g set |
| 10kg/BIB |
10kg/BIB |
| |
|
|
*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).
Flexible type
| |
Y618LD |
Y618H |
Y630D |
| Agent A |
Agent B |
Agent A |
Agent B |
Agent A |
Agent B |
| Application / Properties / Features |
Flexible / Low distortion |
Hight strength / High heat resistance |
| Base |
Acrylic resin |
Acrylic resin |
Acrylic resin |
| External appearance |
Red |
Blue |
Light yellow |
Light green |
Light yellow |
Light green |
| Viscosity |
Pa･s/23°C |
5,000 |
5,000 |
15,000 |
15,000 |
4,000 |
4,000 |
| Mixing ratio |
1:1 |
1:1 |
1:1 |
| Pot life *1 |
23°C |
2 min |
2 min 30 s |
1 min 30 s |
| Set time *2 |
23°C |
7 min |
10 min |
4 min 30 s |
| Adhesive property |
Tensile shear strength |
MPa |
14.2 |
15.7 |
25.3 |
| T-peel strength |
N/mm |
5.9 |
5 |
4.6 |
| Curing properties |
Hardness |
Shore D |
47 |
55 |
83 |
| Glass transfer point |
°C |
61 |
|
118 |
| Elastic modulus |
MPa |
451 |
|
2414 |
| Breaking strength |
MPa |
10.5 |
10.6 |
32.1 |
| Elongation at break |
% |
40 |
51 |
2 |
| Capacity |
600g set |
190mL set |
600g set |
| 10kg/BIB |
|
|
| |
|
|
|
*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).
Conventional type SGA Y650 (*Odorous)
| |
Y650 |
| Agent A |
Agent B |
| Base |
Acrylic resin |
| External appearance |
Blue |
Red |
| Viscosity |
mPa･s/23°C |
3,220 |
3,320 |
| Mixing ratio |
1:1 |
| Pot life *1 |
23°C |
2 min 30 s |
| Set time *2 |
23°C |
4 min 30 s |
| Adhesive property |
Tensile shear strength |
MPa |
23.8 |
| T-peel strength |
N/mm |
4.6 |
| Curing properties |
Hardness |
Shore D |
60 |
| Glass transfer point |
°C |
83 |
| Elastic modulus |
MPa |
740 |
| Breaking strength |
MPa |
16.1 |
| Elongation at break |
% |
25 |
| Capacity |
2.5kg |
*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).